Continuous cast products

Slabs: Cast in single strand slab caster of steel melt shop I. Liquid steel is produced through electric arc furnace-AOD Convertor/VOD-Ladle refining furnace route.

Blooms: Cast from twin stand bloom caster at Steel Melt Shop II. Liquid steel is produced through electric arc furnace-AOD convertor- ladle refining furnance route.

Size: 160 mm sq.
         200 mm sq.

Hot rolled products

HR coils: As cast/ ground slabs are first heated and soaked in reheating furnace, rolled in roughing mill to intermediate thickness and then to the final thickness in the steckel mill.

HRAP Coils: Hot rolled annealed pickled coils are produced after continuous annealing and pickling.

HRAP Plates: No1 finish plates are produced after annealing and pickling or by cutting hot rolled annealed pickled coils to desired lengths.


Cold rolled products

Cold rolled coils and sheets are produced after being processed in the 20 Hi Mill, continuous anneal & pickle line, skin pass mill slitting line and cut to length lines. Absolute flat sheets are produced after being put through the Voss leveller. Sheets & cold rolled coils are available in different finishes 2D, 2B, No3, No4 and BA


Blade steel

The company is the exclusive producer of stainless teel strips for making razor blades and surgical blades in India. The plant has a capacity to produce 10,000 metric tonnes per annum.

JSL can readily supply Stainless Razor Blade Steel as per the broad material specifications / details given below :

(a) Size :
Thickness = 0.10 mm (+/- 0.007 mm)
Width = 22.40 mm (+/- 0.03 mm) and upto 340 mm (Max.)

(b) Chemical Composition :

(c) Rolled Hardness = 280 to 330 HV
(d) Tensile Strength = 95 to 120 Kg/mm sq.
(e) Coil I. D. = 280 mm


Customised products

Jindal Stainless Has developed the capability to supply customized products for critical applications. This has helped customers in their indigenisaation efforts.

Nuclear applications
Special stainless steel was developed for critical components in nuclear applications (304 L, 321 etc.) having very low inclusion content, high corrosion resistance (<10 MPY), ultrasonically sound (w.r.t. angular & straight beam probe testing), high temper tensile strength and impact strength.

Tailor made products
Niobium stabilized special grade austenitic stainless steel was developed for critical components to be used in steam and gas turbines and other engine components. This steel was required to have specified chemical compositions with mechanical and impact properties.

Duplex Stainless Steel
JSL 2205, a ferritic-austentic stainless steel having a high chloride pitting resistance is the new entrant in the product mix. Cold Rolled annealed strips find extensive application as tubular material in sea water, chemical and paper & pulp plants.